What should be paid attention to in the processing of mobile phone plastic shell

Release time:2024-12-11

The surface treatment of plastic products mainly includes coating treatment and coating treatment. Plastics generally have high crystallinity, low polarity or non polarity, and low surface energy, which will affect the adhesion of the coating. Because plastic is a non-conductive insulator, it cannot be coated directly on the surface of plastic according to the technical standard of electroplating. Therefore, before surface treatment, necessary pretreatment should be carried out to improve the adhesion of coating and provide a conductive bottom layer with excellent adhesion for coating.

1. Pretreatment of coating

Pretreatment includes degreasing treatment of plastic surface, that is, cleaning the oil stain and release agent on the surface, and activation treatment of plastic surface, in order to improve the adhesion of coating.

(1) Degreasing of plastic products

Similar to the surface degreasing of metal products, the degreasing of plastic products can be cleaned with organic solvents or alkaline aqueous solution containing surfactant. Organic solvent degreasing is applicable to the cleaning of white wax, beeswax, fat and other organic dirt on the surface of plastic. The organic solvent used should be insoluble, non swelling, non cracking, low boiling point, volatile, non-toxic and non combustible.

Alkaline aqueous solution is suitable for degreasing alkali resistant plastics. The solution is rich in caustic soda, alkaline salts and various externally active substances. The most commonly used surface active substances are OP series, namely alkyl phenol polyoxyethylene ether, which will not form foam and will not remain on the plastic surface.

(2) Activation of the appearance of plastic products

This activation is to improve the surface properties of the plastic, that is, generate some polar groups on the surface of the plastic or coarsen it, so that the coating is easier to be wetted and adsorbed on the surface of the parts. The method of surface activation treatment.

Many, such as chemical oxidation, flame oxidation, solvent vapor etching and corona discharge oxidation. Among them, the chemical crystal oxidation treatment method is widely used. The commonly used method is chromic acid treatment solution. Its typical formula is potassium dichromate 4.5%, water 8.0%, concentrated sulfuric acid (more than 96%) 87.5%.

Some plastic products, such as polystyrene and ABS plastic, can also be directly coated.

In order to obtain high-quality coating, chemical oxidation treatment is also useful. For example, ABS plastic can be etched with dilute chromic acid treatment solution after degreasing. Its typical treatment formula is chromic acid 420 g / L and sulfuric acid (specific gravity 1.83) 200 ml / L. The typical treatment process is 65 ℃ 70 ℃ / 5 minutes and 10 minutes, washed with water and dry.

The advantage of chromic acid treatment solution etching is that no matter how messy the shape of plastic products is, they can be treated uniformly. The disadvantage is that the operation is risky and there is doubt of pollution.


2. Pretreatment of coating

The purpose of coating pretreatment is to improve the adhesion between the coating and the plastic surface, so that the plastic surface forms a conductive metal bottom layer. The first step of pretreatment process is rich in: mechanical coarsening, chemical degreasing, chemical coarsening, sensitization, activation, recovery and electroless plating. The first three items are to improve the adhesion of the coating, and the last four items are to form a conductive metal bottom layer.

(1) Mechanical and chemical roughening

Mechanical coarsening and chemical coarsening are to coarsen the plastic surface by mechanical and chemical methods respectively, so as to increase the contact area between the coating and the substrate. It is generally believed that the binding force achieved by mechanical coarsening is only about 10% of that achieved by chemical coarsening.

(2) Chemical degreasing

The oil removal method of plastic surface coating before coating is the same as that of coating before coating.

(3) Sensitization

Sensitization is to make the plastic surface with certain adsorption capacity absorb some easily oxidized substances, such as tin dichloride, titanium trichloride, etc. These adsorbed oxidizable substances are oxidized during the activation process, and the activator is reduced to catalytic nuclei, which are retained on the surface of the product. The role of sensitization is to lay a foundation for subsequent electroless plating of metal layers.

(4) Activation

Activation is the treatment of the sensitized surface with a solution of catalytically active metal compounds. Essentially, the product adsorbed with the restoring agent is immersed in the oxidant aqueous solution rich in precious metal salts, so that the precious metal ions as the oxidant are restored by S2 n. The restored precious metal is colloidal particles accumulated on the surface of the product, which has strong catalytic activity. When the surface is immersed in the electroless plating solution, these particles become the catalytic intermediate, which accelerates the reaction speed of electroless plating.

(5) Recovery Disposal

Before electroless plating, dip the product cleaned with clean water after activation treatment into a certain concentration of reductant solution for electroless plating to recover and remove the uncleaned activator, which is called recovery treatment. Formaldehyde solution is used for recovery treatment during electroless copper plating, and sodium hypophosphite solution is used for recovery treatment during electroless nickel plating.

(6) Electroless plating

The purpose of electroless plating is to form a conductive metal film on the outer surface of plastic products and create conditions for electroplating the metal layer of plastic products. Therefore, electroless plating is the key process of plastic electroplating.


Copyright: Shenzhen Zhongyuan Plastic Co., Ltd. | mold processing customized manufacturer. If you want to know the processing price of the factory, how much is it, and which is good, please contact us Yue ICP Bei No. 17060480
美女被肏哭视频在线观看| 日韩一级片在线免费观看| av天堂人妻一区二区三区| 成人亚洲综合av电影网| 久久天天躁狠狠躁夜夜爽| 亚洲欧洲日产国码高潮AV| 国产精品黑丝美女啪啪啪| 一级毛片久久| 国产精品爱搞视频网网址| 好嗨哟直播看片在线观看| 亚洲综合av每日更新网| 国产在线精品成人一区二区三区| 俺也去在线视频免费观看| 国产一二三区精品亚洲美女| 亚洲免费一级片中文字幕| 欧美色综合天天在线影院| 亚洲av国产av综合av| 亚洲第一AV国| 国产精品久久久久久久久久久不卡| 国产精品制服丝袜四区 | dxj在线视频免费观看| 午夜福利啪啪无遮挡免费| 黄色中文字幕一区二区三区| 最新自拍成人在线看片网| 91国内精品线免费播放| 综合99综合久久久久久久| 国产极品尤物a在线观看| 欧美成人a猛片在线播放| 99这里有精品免费视频| 国产精品一区二区三区免费| 成人午夜精品视频在线观看| 国产区一区二区三区高清| 91精品国产综合久久久久| 99热在线精品免费全部| gogo亚洲高清人体艺术| 亚洲综合精品一区二区在线| 麻豆欧美精品国产综合久久| 动漫精品3d在线网址黄| 国产免费久久久久久无码| 国产精品天天影视久久综合| 日韩啪啪午夜激情福利片|